注塑成型、热压成型、喷塑成型、热压成型是最重要的原材料
耐火PC塑料原材料
聚碳酸酯树脂（PC塑料原料）是一种优良的工程热塑性塑料，具有良好的抗冲击性、易加工性、良好的尺寸稳定性、高耐热性、无毒性、低吸水性和良好的介电性能。在五大关键工程塑料（PA、PC、PBT、POM、PPO）中，聚碳酸酯被公认为唯一具有良好透明度的产品，近年来占据了最快速的市场增长
性能：复合聚碳酸酯PC塑料颗粒，具有高透明度、高冲击性、高强度、高蠕变性、优异的尺寸稳定性、良好的耐低温和耐热性、阻燃性
个人电脑分类：
★ 防静电PC塑料原材料★导电PC塑料原材料★加纤维防火PC塑料原材料★紫外线风化PC塑料原材料★食品级PC塑料原料★防化PC塑料原材料
耐火PC塑料原材料制造商和工厂
测试标准
| 66MPa | ASTM D-638 | |||||||||
| 弯曲强度 | 103MPa | ASTM D-790style=“border left:none”colspan=“3”>15% | ASTM D-638 | |||||||
| 弯曲模量 |
||||||||||
| ASTM D-150 | ||||||||||
| 体积电阻率 | 1.0<。cm | ASTM D-257 |
Fire Resistant PC Plastic Raw Materials
PC usually is made into products by injection molding, extrusion, coining, blow molding, thermoforming,
printing, adhesive, coating and machining, the most important processing method is injection molding
Fire Resistant PC Plastic Raw Materials
Product Details
Specifications
Polycarbonate Resin (PC Plastic Raw Materials) is an excellent engineering thermoplastic, with fine impact resistance, easily processing, good dimensional stability, high heat resistance, non-toxic, low water absorption and good dielectric properties. Being recognized as the only one with good transparency in the five key engineering plastics (PA, PC, PBT, POM, PPO), polycarbonate occupies the most rapid market growth in recent years.
Property: Compound Polycarbonate PC Plastic Granule with high transparency, high impact, high strength, high creep resistance, excellent dimensional stability, good resistance to low-temperature and heat, flame retardant.
PC Classification:
★ Anti-static PCPlastic Raw Materials
★Conductive PCPlastic Raw Materials
★Plus fiber fire PCPlastic Raw Materials
★UV weathering PCPlastic Raw Materials
★Food-grade PCPlastic Raw Materials
★Anti-chemical PCPlastic Raw Materials
Fire Resistant PC Plastic Raw Materials Manufacturers and Factory
Testing Standard
| Item | Typical Characteristic | |||||||
| Density | 1.25g/cm3 | ASTM D-792 | ||||||
| MoldingShrinkage | 0.002-0.004mm/mm | ASTM D-955 | ||||||
| Water Absorption | 0.12% | ASTM D-570 | ||||||
| Rockwell Hardness | 124 | ASTM D-785 | ||||||
| Tensile Strength | 66MPa | ASTM D-638 | ||||||
| FlexuralStrength | 103MPa | ASTM D-790 | ||||||
| Elongation at break | 15% | ASTM D-638 | ||||||
| Flexural Modulus | 3445MPa | ASTM D-790 | ||||||
| Izod Notched Impact Strength | 107J/m | ASTM D-256 | ||||||
| Heat Deflection Temperature | 146℃ | ASTM D-648 | ||||||
| Permittivity | 3.1(60Hz) | ASTM D-150 | ||||||
| Loss Factor | 0.0008（60Hz） | ASTM D-150 | ||||||
| Volume Resistivity | 1.0×10^17Ω.cm | ASTM D-257 | ||||||