碳纤维增强尼龙6原材料

产品详细信息

碳纤维增强尼龙6原材料

由于尼龙6容易吸收水分，因此在加工前应特别注意确保其完全干燥。如果材料采用防水材料包装，则容器应保持密封。如果湿度大于0.2，建议在80℃以上的热空气中干燥16小时。如果材料暴露在空气中超过8小时，建议真空干燥超过105摄氏度8小时。尼龙6注射成型工艺的熔体温度：240-250°C，改良品种为250-280°C。

预干燥：在90°C温度下4小时，除了直接从容器进料；尼龙吸收水分，应储存在防潮容器和密闭料斗中；水含量超过0.25%将导致成型变化
可提供进料，使回收率提高10%
如果提供的温度超过60°C，产品应逐渐冷却；逐渐冷却可以减少成型后的收缩。收缩率：0.7-2.0；或30%玻璃纤维，收缩率0.3-0.8；如果提供的温度超过60°C，产品应逐渐冷却；逐渐冷却可以减少成型后的收缩。也就是说，产品具有更高的尺寸稳定性和更小的内应力；首选蒸汽法；尼龙塑料制品可以使用焊剂检查应力

是专业的碳纤维增强尼龙6原材料制造商之一，您可以从我们工厂以优惠的价格订购高品质的碳纤维增强尼龙6原材料

Carbon Fiber Reinforced Pa6 Raw Material

.
PA6 Plastic Material
Thermoplastic, lightweight, tough, chemical and durable
Good wear resistance, self-lubricating and solvent resistance
Free Sample and express delivery

Carbon Fiber Reinforced Pa6 Raw Material

Product Details

carbon fiber reinforced pa6 raw material

Because nylon 6 is prone to absorbing moisture, great care should be taken to ensure that it is completely dry before processing. The container should be kept airtight if the material is supplied with waterproof material packaging. It is recommended to dry in hot air above 80 C for 16 hours if the humidity is greater than 0.2. Vacuum drying for more than 105 C,8 hours is advised if the material has been exposed to air for more than 8 hours. Melt temperature for Nylon 6 injection molding process: 240-250°C, for improved varieties 250-280°C.

Pre-drying: 4 hours at 90°C temperature, in addition to feeding directly from the container; nylon absorbs moisture and should be stored in a moisture-proof container and a closed hopper; water comprising more than 0.25 percent will cause molding changes.
Feed can be supplied to increase the recovery rate by 10%.
If the temperature provided exceeds 60°C, the product should be gradually cooled; gradual cooling can reduce shrinkage after molding. Contraction rate:0.7-2.0; or 30% glass fiber, shrinkage 0.3-0.8; if the temperature provided exceeds 60°C, the product should be gradually cooled; gradual cooling can reduce shrinkage after molding. That is, the product has higher dimensional stability and has less internal stress; the steam method is preferred; nylon plastic items can be checked for stress using flux.

is one of the professional carbon fiber reinforced pa6 raw material manufacturers, you can order high quality carbon fiber reinforced pa6 raw material at good price from our factory.